Sample ID |
Material |
Size of grain |
Comment |
Dm(mass fractal dimesion) |
Ds(surface fractal dimesion) |
157k
family |
SiC |
3.9 nm |
powder synthesized from organic precursors |
|
|
157k |
SiC |
3.9 nm |
powder manually pressed during sample preparation |
0.685(9) |
2.04(1) |
157kbis |
SiC |
3.9 nm |
powder manually pressed during sample preparation |
0.63(1) |
1.98(1) |
157k-F1 |
SiC |
3.9 nm |
powder not pressed ("F"=1) |
1.80(1) |
2.04(1) |
157k-F2 |
SiC |
3.9 nm |
powder pressed a little ("F"=2) |
1.23(1) |
1.984(9) |
157k-F3 |
SiC |
3.9 nm |
powder pressed heavily ("F"=3) |
0.42(1) |
1.96(1) |
157k-F4 |
SiC |
3.9 nm |
powder pressed heavily ("F"=4) |
0.73(1) |
1.920(8) |
h1k |
SiC |
2.0 nm |
powder synthesized from organic precursors, manually pressed during
sample preparation |
0.41(4) |
2.12(1) |
w3k |
SiC |
2.7 nm |
powder synthesized from organic precursors, manually pressed during
sample preparation |
0.75(2) |
2.14(1) |
98-g1 |
SiC |
nm |
powder |
|
|
GaN-500-old |
GaN |
nm |
powder |
1.471(9) |
2.23(2) |
max-9711
family |
SiC |
microns |
nano-SiC sintered at MAX80 6-anvill press (Hasylab/DESY) |
|
|
max-9711-01SI |
SiC |
|
|
|
2.43(1) |
max-9711-02SI |
SiC |
|
|
|
2.164(8) |
max-9711-03KI |
SiC |
|
|
|
2.33(1) |